Wear and corrosion resistance of laser remelted and plasma sprayed Ni and Cr coatings on copper
LIANG Gong-ying(梁工英)1, T.T.WONG (黄俊达)2
AN Gen(安  耿)1
(1. Department of Materials Physics, Science School,
 Xi’an Jiaotong University, Xi’an 710049, China;
2. Department of Mechanical Engineering, The Hong Kong Polytechnic University, Hong Kong, China
)
Abstract: Nickel and chromium coatings were produced on the copper sheet using plasma spraying and laser remelting. The sliding wear test was achieved on a block-on-ring tester and the corrosion test was carried out in an acidic atmosphere. The corrosive behaviors of both coatings and original copper samples were investigated by using an impedance comparison method. The experimental results show that the nickel and chromium coatings display better wear resistance and corrosion resistance relative to the original pure copper sample. The wear resistance of the coatings is 8-12 times as large as original samples, and the wear resistance of laser remelted samples is better than that of plasma sprayed ones. The corrosion resistance of laser remelted nickel and chromium samples is better than that of plasma sprayed samples respectively. The corrosion rate of chromium coatings is less than that of nickel coatings, and the laser remelted Cr coating exhibits the least corrosion rate.
Key words: corrosion; wear; laser remelting; plasma spraying