Fabrication of AZ61-1.0%Y antiburning magnesium semisolid slurry
(1. Key Laboratory of Ministry of Education for Conveyance and Equipment,
East China Jiaotong University, Nanchang 330013, China
2. School of Mechanical and Electrical Engineering, Nanchang University, Nanchang 330031, China3
3. Key Laboratory of Superlight Materials and Surface Technology of Ministry of Education,
Harbin Engineering University, Harbin 150001, China)
East China Jiaotong University, Nanchang 330013, China
2. School of Mechanical and Electrical Engineering, Nanchang University, Nanchang 330031, China3
3. Key Laboratory of Superlight Materials and Surface Technology of Ministry of Education,
Harbin Engineering University, Harbin 150001, China)
Abstract: The semi-solid antiburning AZ61-1.0%Y magnesium alloy slurry with fine circular solid phase was fabricated by a novel type continuous mechanical stirring in this work. The microstructure of the semisolid slurry was characterized by a metallography microscope. The results show that the fine circular solid phase distributes uniformly in the slurry when the stirring temperature ranges from 600 to 605 ˚C. With the increase of the stirring velocity, the size of the solid phase becomes smaller and smaller. With the increase of the stirring time, the size of solid phase gets finer, but if the stirring time is longer than the critical time, it will be coarsened abnormally. The mechanical properties of semi-solid AZ61-1.0%Y alloy are superior to those of the normally casting magnesium alloy.
Key words: semi-solid; continuous mechanical stir; microstructure; mechanical properties