Surface characteristics of chemical conversion coating for Mg-Al alloy
(1. Nagoya University, Furo-cho, Chikusa-ku, Nagoya, 464-8603, Japan;
2. Division of Marine Engineering, Mokpo Maritime University, Mokpo City, Jeonnam, 530-729, Korea)
2. Division of Marine Engineering, Mokpo Maritime University, Mokpo City, Jeonnam, 530-729, Korea)
Abstract: The chemical conversion coating was formed on Mg alloy for low cost and harmlessness in environment by using the colloidal silica as the main component. The film formed at 298 K was thick, which was thought to be the combination of Si and O. In salt spray test, the ratio of black rust on the specimen that did not conducted chemical conversion treatment was five times or more than those of the chemical conversion treated specimen. The film of chemical conversion coating produced by alkali treatment process was thinner than the specimen produced in basic chemical conversion treatment solution.
Key words: chemical conversion coating; Mg alloy; salt spray test; alkali treatment