Subsequent yield loci of 5754O aluminum alloy sheet
(School of Mechanical Engineering and Automation, Beihang University, Beijing 100191, China)
Abstract: Complex loading paths were realized with cruciform specimens and biaxial loading testing machine. Experimental method for determining the subsequent yield locus of sheet metal was established. With this method, the subsequent yield loci of 5754O aluminum alloy sheet were obtained under complex loading paths. Theoretical subsequent yield loci based on Yld2000-2d yield criterion and three kinds of hardening modes were calculated and compared with the experimental results. The results show that the theoretical subsequent yield loci based on mixed hardening mode describe the experimental subsequent yield loci well, whereas isotropic hardening mode, which is widely used in sheet metal forming fields, predicts values larger than the experimental results. Kinematic hardening mode predicts values smaller than the experimental results and its errors are the largest.
Key words: aluminum alloy sheet; complex loading path; subsequent yield locus; hardening mode