Interface characteristic of friction stir welding lap joints of
Ti/Al dissimilar alloys
Ti/Al dissimilar alloys
(National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology,
Nanchang Hangkong University, Nanchang 330063, China)
Nanchang Hangkong University, Nanchang 330063, China)
Abstract: Lap joints of TC1 Ti alloy and LF6 Al alloy dissimilar materials were fabricated by friction stir welding and corresponding interface characteristics were investigated. Using the selected welding parameters, excellent surface appearance forms, but the interface macrograph for each lap joint cross-section is different. With the increase of welding speed or the decrease of tool rotation rate, the amount of Ti alloy particles stirred into the stir zone by the force of tool pin decreases continuously. Moreover, the failure loads of the lap joints also decrease with increasing welding speed and the largest value is achieved at welding speed of 60 mm/min and tool rotation rate of 1500 r/min, where the interfacial zone can be divided into 3 kinds of layers. The microhardness of the lap joint shows an uneven distribution and the maximum hardness of HV 502 is found in the middle of the stir zone.
Key words: interface characteristic; Ti/Al dissimilar alloys; friction stir welding; lap joint