Magnetic and mechanical properties of FeSi alloys with high Si content
(1.School of Materials Science and Engineering,Beijing University of Aeronautics and Astronautics, Beijing 100083, China2.北京市北京航空航天大学材料科学与工程学院)
Abstract: The chemical vapor(CVD) deposition-diffusion method was applied to prepare FeSi alloys with high silicon content up to 6.5%. In spite of various deposition and post-annealing, the sample remains α-Fe bcc structure. The cross section of the composition was analyzed to evaluate the Si content and distribution before and after annealing. The results show that the soft magnetic properties are improved by increasing the silicon content. For the samples containing about 6.5% Si, the coercivity decreases to 60 from 237.3 A/m of the original. It is also obtained that, in addition to the Si content, Si distribution has a large influence on the core loss due to the effect of resistivity. The micro-hardnesses were also evaluated along the cross-section after various annealings.
Key words: FeSi alloy; chemical vapor deposition; diffusion; magnetic properties; micro-hardness