Effect of evolution of polycrystalline textures on r-value of LF2 aluminum alloy
(1.上海市上海交通大学机械工程学院
2.School of Mechanical Engineering, Shanghai Jiao Tong University, Shanghai 200240, China)
2.School of Mechanical Engineering, Shanghai Jiao Tong University, Shanghai 200240, China)
Abstract: The effect of evolution of polycrystalline texture on normal anisotropy coefficient r-value of aluminum alloy sheet was investigated. For this purpose, the textures under different elongation of LF2 aluminum alloy were measured and analyzed. The result indicates that the initial texture of LF2 aluminum alloy has the typical rolling texture, and the main components include Brass {011}〈211〉, Copper {112}〈111〉and S{123}〈634〉. These three main components exhibit different transformation tendencies when the material specimens are stretched along the different direction. Based on Taylor model and Minor Work principle, the normal anisotropy coefficient r-values of polycrystalline aluminum alloy under various strain states were calculated. The result indicates that the r-values of LF2 aluminum alloy vary with tensile direction and the amount of deformation. The deformability on rolling direction is superior to the other direction because an enhancement tendency of r0 appears in tension process along rolling direction.
Key words: polycrystalline texture; normal anisotropy coefficient; uniaxial tensile; deformability; LF2 aluminum alloy