Preparation of poly(propylene carbonate)/organophilic rectorite nanocomposites via direct melt intercalation
(1.School of Chemical Engineering and Pharmacy, Wuhan Institute of Chemical Technology, Wuhan 430073, China
2.College of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China)
2.College of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China)
Abstract: The completely degradable nanocomposites comprised of poly(propylene carbonate)(PPC) and organo-modified rectorite (OREC) were prepared by direct melt intercalation. The structure and mechanical properties of PPC/OREC nanocomposites were investigated. The wide-angle X-ray diffraction (WAXD) results show that the galleries distance of OREC is increased after PPC and OREC melt intercalation, which indicates that PPC molecular chain has intercalated into the layers of OREC. The PPC/OREC nanocomposites with lower OREC content show an increase in thermal decomposition temperature compared with pure PPC. The tensile strength and impact strength of PPC/OREC nanocomposites are improved. When the mass fraction of OREC is 4%, the tensile strength and impact strength of the PPC/OREC nanocomposite increase by 22.86% and 48.58% respectively, compared with pure PPC.
Key words: poly(propylene carbonate); rectorite; degradation; nanocomposites