Microstructural and abrasive wear properties of SiC reinforced aluminum-based composite produced by compocasting
(Karaj Branch, Islamic Azad University, Karaj, Iran)
Abstract: The effect of SiC particles reinforcement with average size of 1, 5, 20 and 50 μm and volume fraction of 5%, 10% and 15% on the microstructure and tribological properties of Al-based composite was investigated. Composites were produced by applying compocasting process. Tribological properties of the unreinforced alloy and composites were studied using pin-on-disc wear tester, under dry sliding conditions at different specific loads. The influence of secondary mechanical processing with different rolling reductions on the dry sliding wear characteristics of Al matrix composites was also assessed. Hardness measurement and scanning electron microscopy were used for microstructural characterization and investigation of worn surfaces and wear debris. The proper selection of process parameter such as pouring temperature, stirring speed, stirring time, pre-heated temperature of reinforcement can all influence the quality of the fabricated composites. The porosity level of composite should be minimized and the chemical reaction between the reinforcement and matrix should be avoided.
Key words: aluminum matrix composite; hardness; wear; Al 6061; SiC particles