Preparation and oxidation resistance of B2O3-coated boron-modified carbon foams
(C/C Composites Technology Research Center, state Key Laboratory of solidification processing,
Northwestern Polytechnical University, Xi’an 710072, China)
Northwestern Polytechnical University, Xi’an 710072, China)
Abstract: To improve the oxidation resistance of boron-modified carbon foams, the B2O3 coating was prepared on boron-modified carbon foams by low-cost slurry method. The microstructures and phase compositions of the coated carbon foams were characterized by scanning electron microscopy and X-ray diffraction, respectively. Oxidation resistances of uncoated and coated boron-modified carbon foams were investigated at 873 K in air. The results showed that as-received B2O3 coating could protect boron-modified carbon foams from oxidation at 873 K. B2O3-coated carbon foam doped with 7% B2O3 (mass fraction) (BO-7) had better oxidation resistance, exhibiting mass loss of 17.40% after oxidation at 873 K for 120 min. The melting glass layer formed on the surface of BO-7 could prevent oxygen from diffusing into boron-modified carbon foams substrate during oxidation to some extent.
Key words: carbon foam; B2O3; coating; oxidation resistance