Effect of carbon and boron additions on segregation behavior of irectionally solidified nickel-base superalloys with rhenium
(1. State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China;
2. Ningbo Branch of China Academy of Ordnance Science, Ningbo 315103, China)
2. Ningbo Branch of China Academy of Ordnance Science, Ningbo 315103, China)
Abstract: The phase transformation temperature, segregation behavior of elements and as-cast microstructure were investigated in experimental nickel-base superalloys with different levels of carbon and boron. The results show that the liquidus temperature decreases gradually but the carbide solvus temperature increases obviously with increasing carbon addition. Minor boron addition to the alloy decreases the liquidus temperature, carbide solvus temperature and solidus temperature slightly. Apart from rhenium, the segregation coefficients of the elements alter insignificantly with the addition of carbon. The segregation behavior of rhenium, tungsten and tantalum become more severe with boron addition. The volume fraction and size of primary carbides increase with increasing carbon addition. The main morphology of the carbides is script-like in the alloys with carbon addition while the carbide sheets tend to be concentrated and coarse in the boron-containing alloys.
Key words: carbon; boron; segregation behavior; directional solidification; nickel-base superalloys