Preparation and characterization of Ce1-xDyx-ySryO2-δ system
(1. School of Physics, University of Hyderabad, Hyderabad 500046, India;
2. Department of Physics, Osmania University, Hyderabad 500007, India)
2. Department of Physics, Osmania University, Hyderabad 500007, India)
Abstract: The effect of dysprosium and strontium on the total ionic conductivity of ceria in the system Ce1-xDyx-ySryO2-δ was studied. In this system, few compositions were prepared with x=0.15, y=0.015, 0.03 and 0.045 by modified sol-gel process using maltose and pectin as organic precursors. Rietveld refinement of XRD patterns confirms the cubic structure with space group . SEM images show relatively uniform grains with clean and distinct grain boundaries. Four probe AC impedance measurements were carried out to evaluate the total ionic conductivity in the temperature range of 150-500 °C and frequency range of 40 Hz-1 MHz. The composition Ce0.85Dy0.12Sr0.03O2-δ shows higher electrical conductivity than single-doped ceria samples.
Key words: electrolyte; Sr-Dy doping; impedance spectroscopy; conductivity