Internal residual stress measurement on linear friction welding of titanium alloy plates with contour method
(1. Provincial Key Lab of Advanced Welding Technology, Jiangsu University of Science and Technology,
Zhenjiang 212003, China;
2. China Friction Stir Welding Center, Beijing 100024, China)
Zhenjiang 212003, China;
2. China Friction Stir Welding Center, Beijing 100024, China)
Abstract: The internal residual stress within a TC17 titanium alloy joint welded by linear friction welding (LFW) was measured by the contour method, which is a relatively new and destructive technique to obtain a full map of internal residual stress. The specimen was first cut into two parts; the out-of-plane displacement contour formed by the release of the residual stress was then measured; finally, taking the measured contour of the cut plane as the boundary conditions, a linear elastic finite element analysis was carried out to calculate the corresponding distribution of residual stress normal to the cut plane. The internal stress distribution of the TC17 titanium alloy LFW joint was also analyzed. The results show that the tensile residual stress in the TC17 LFW weld is mainly present within a region about 12 mm from the weld centerline; the peak tensile residual stress occurs at the weld centerline and reaches 360 MPa (about one third of the yield strength of TC17 alloy); within the weld zone of the TC17 LFW weld, the through-thickness stress is not uniform, and the internal stress is larger than that near the top or bottom surface.
Key words: residual stress; linear friction welding; titanium alloy; contour method