Zr-Co(Cu)-Al bulk metallic glasses with optimal glass-forming ability and their compressive properties
(School of Materials Science and Engineering, Center of Excellence for High Strength Alloys Technology, Iran University of Science and Technology, Tehran 1684613114, Iran)
Abstract: The formation of bulk metallic glasses (BMGs) in the ternary Zr56Co28Al16 and quaternary Zr56Co28-xCuxAl16 (x=2, 4, 5, 6, 7, mole fraction, %) glassy alloys was investigated via the copper mold suction casting method. The main purpose of this work was to locate the optimal BMG-forming composition for the quaternary ZrCo(Cu)Al alloys and to improve the plasticity of the parent alloy. The X-ray diffractometry (XRD), transmission electron microscopy (TEM) and differential scanning calorimetry (DSC) were used to investigate the glassy alloys structure and their glass forming ability (GFA). In addition, the compression test, microhardness, nano-indentation and scanning electron microscopy (SEM) were utilized to discuss the possible mechanisms involved in the enhanced plasticity achievement. The highest GFA among Cu-containing alloys was found for the Zr56Co22Cu6Al16 alloy, which was similar to that of the base alloy. Furthermore, the plasticity of the base alloy increased significantly from 3.3% to 6% for the Zr56Co22Cu6Al16 BMG. The variations in the plasticity and GFA of the alloys were discussed by considering the positive heat of mixing within Cu and Co elements.
Key words: bulk metallic glass; zirconium base alloy; glass forming ability; plasticity