Effects of under-aging treatment on microstructure and mechanical properties of squeeze-cast Al-Zn-Mg-Cu alloy
(1. School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China;
2. Key Laboratory for Advanced Materials Processing Technology, Ministry of Education, Tsinghua University, Beijing 100084, China)
2. Key Laboratory for Advanced Materials Processing Technology, Ministry of Education, Tsinghua University, Beijing 100084, China)
Abstract: The effects of under-aging treatment on the microstructure and mechanical properties of Al-Zn-Mg-Cu alloy produced by squeeze casting were investigated using optical microscopy (OM), X-ray diffractometry (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and hardness and tensile testing. The results showed that most of secondary phases were dissolved into α(Al) matrix while no significant grain growth happened under the condition of solution treatment at 470 °C for 4 h. Due to the strengthening effect of GP zones, for alloys treated by under-aging process, the increase of aging time and aging temperature improved the ultimate tensile strength (UTS) and yield strength (YS), but decreased the elongation (δ) to some extent. By utilizing appropriate aging time and temperature, the best combination of strength and ductility could be obtained to fulfill the design requirements of automobile components.
Key words: Al-Zn-Mg-Cu alloy; squeeze casting; under-aging treatment; GP zone; precipitation strengthening