Microstructure, texture and mechanical properties of Mg-8Gd-4Y-1Nd-0.5Zr alloy prepared by pre-deformation annealing, hot compression and ageing
Yi-ping WU1, Han-qing XIONG1, Yu-zhen JIA2, Shao-hui XIE1, Guo-feng LI1
(1. Department of Mechanical and Electrical Engineering, Changsha University, Changsha 410022, China;
2. Bichamp Cutting Technology (Hunan) Co., Ltd., Changsha 410200, China
)
Abstract: An extruded Mg-8Gd-4Y-1Nd-0.5Zr alloy was pre-heated at 470 °C for 1 h and subsequently compressed at 470 °C and two strain rates of 0.2 and 0.0003 s-1. Microstructure, texture and mechanical properties of the alloy were examined by optical microscopy (OM), scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), hardness test and tensile test. The results show that the post-deformed microstructures of alloy are non-uniform at both strain rates due to the dissolution of RE-rich particles and the occurrence of DRX. The textures of post-deformed alloy are affected by strain rate. The alloy exhibits a strong basal texture of á0001?//ND (normal direction) after compression at 0.2 s-1, while a weak texture component of á0001?//ED (extrusion direction) is formed in the compression obtained at 0.0003 s-1. Compared with the alloy compressed at 0.0003 s-1, the compressed alloy obtained at 0.2 s-1 presents better comprehensive mechanical properties with the ultimate tensile strength of 426 MPa, yield strength of 345 MPa and ductility of 2.1% when being aged at 225 °C for 8 h.
Key words: magnesium alloys; strain rate; microstructure; texture; mechanical properties