Effect of iron valence on hydrothermal preparation of pyrochlore-type tungsten oxide
(School of Metallurgy and Environment, Central South University, Changsha 410083, China)
Abstract: Pyrochlore-type tungsten oxide (PTO), WO3·0.5H2O, is an emerging material with very wide potential applications. The influences of iron valences and the additive amount of ferrous ion on tungsten crystallization ratio and the acceleration mechanism of ferrous ion were investigated when PTO was hydrothermally prepared in aqueous ammonium tungstate solution containing ammonium carbonate. The results show that ferrous ion can remarkably accelerate tungsten crystallization while both elemental iron and ferric ion have little influence on the crystallization. Moreover, the tungsten crystallization ratio increases with increasing the amount of ferrous ions added and reaches the maximum of about 60% with ferrous ion concentration of 16 g/L. FTIR analysis of the spent solution after PTO crystallization shows that ferrous ion can accelerate the conversion of WO4 tetrahedral to WO6 octahedron. Combined with XPS and XRD analyses of the hydrothermal product, the acceleration effect of ferrous ion on tungsten crystallization could basically be attributed to the increase in the interplanar spacing of PTO lattice caused by the incorporation of ferrous ion into PTO crystal lattice. The results presented is conducive to the efficient preparation of PTO powder and cleaner tungsten metallurgy.
Key words: pyrochlore-type tungsten oxide; ammonium tungstate solution; ferrous ion; crystallization; mechanism