Local corrosion mechanism of SiO2-based refractories caused by slag movement near solid–liquid–gas interface in different slag systems
(Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing 100083, China)
Abstract: Slag movement on SiO2-based prism refractories in different slag systems was observed. The cross section shape evolution mechanism was discussed. Two types of shape evolution appear. For PbO-SiO2 slag whose surface tension improves with SiO2 concentration, slag film flows up along four edges under axial Marangoni shear force and wettability. Then, it flows down along four lateral faces under gravity. Corrosion rate at edges is larger than that on lateral faces due to different SiO2 solubilities of ascending and descending flow. Prism cross section shape changes from square to round. For FetO-SiO2 slag whose surface tension reduces with the increase of SiO2 concentration, slag film flows up under the inflence of wettability. Then, it flows down under Marangoni shear force and gravity. Compared to four edges, slag is mainly up and down on four lateral faces due to larger surface tension and size. So, prism cross section shape keeps square.
Key words: Marangoni convection; slag film; local corrosion; solid-liquid-gas interface; SiO2-based refractories