Characteristics and formation mechanisms of defect bands in vacuum-assisted high-pressure die casting AE44 alloy
(1. Hubei Key Laboratory of Advanced Technology for Automotive Components, Wuhan University of Technology, Wuhan 430070, China;
2. School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China)
2. School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China)
Abstract: The microstructure in vacuum-assisted high-pressure die casting (HPDC) Mg-4Al-4RE (AE44) alloy was studied. Special attention was paid to the characteristics of defect bands and their formation mechanisms. Since double defect bands are commonly observed, the cross section of die cast samples is divided into five parts with different grain morphologies and size distributions. The inner defect band is much wider than the outer one. Both the defect bands are solute segregation bands, resulting in a higher area fraction of Al11RE3 phase than that in the adjacent regions. No obvious aggregation of porosities is observed in the defect bands of AE44 alloy. This may be due to a narrow solidification temperature range of AE44 alloy and a large amount of latent heat released during the precipitation of intermetallic phases. The formation of the defect bands is related to the shear stress acting upon the partially solidified alloy, which can lead to collapse of the grain network. However, the generation mechanisms of shear stress in the outer and inner defect bands are quite different.
Key words: high-pressure die casting; magnesium alloy; AE44; microstructure; defect band