FeNiCrCoSi_x and FeNiCrCoTi_x (x=0, 0.3, 0.6, and 0.9 wt.%) high entropy alloys (HEAs) were prepared via the powder metallurgy technique. A homogenous distribution of the elements in all alloys due to the formation of a solid solution phase is observed. The density and hardness of the prepared HEAs are improved by Si and Ti additions, compared to FeNiCrCo HEA. The wear rate of the prepared alloys was studied at different loads and the results indicate that the alloys that contain 0.3 wt.% Si and 0.9 wt.% Ti have the lowest wear rates. X-ray diffraction, SEM, and EDX were used to understand the phases, grain sizes, and microstructures in different investigated HEAs. The effects of Si and Ti content on the corrosion behavior and surface morphologies of sintered FeNiCrCoSi_x and FeNiCrCoTi_x HEAs were studied by immersion in H₂SO₄, HNO₃, and HCl solutions. Uniform corrosion and localized pitting are observed in different sizes in the corrosive media used. Because of the smaller pit size and the reduced pit density, the FeNiCrCoSi_0.3 HEA has an excellent microstructure.